RESUMO
Bioplastics were developed to overcome environmental problems that are difficult to decompose in the environment. This study analyzes Thai cassava starch-based bioplastics' tensile strength, biodegradability, moisture absorption, and thermal stability. This study used Thai cassava starch and polyvinyl alcohol (PVA) as matrices, whereas Kepok banana bunch cellulose was employed as a filler. The ratios between starch and cellulose are 10:0 (S1), 9:1 (S2), 8:2 (S3), 7:3 (S4), and 6:4 (S5), while PVA was set constant. The tensile test showed the S4 sample's highest tensile strength of 6.26 MPa, a strain of 3.85%, and a modulus of elasticity of 166 MPa. After 15 days, the maximum soil degradation rate in the S1 sample was 27.9%. The lowest moisture absorption was found in the S5 sample at 8.43%. The highest thermal stability was observed in S4 (316.8°C). This result was significant in reducing the production of plastic waste for environmental remediation.